Itauba Wood Fiber (<i>Mezilaurus lindaviana</i>) and Itauba Wooden Board: A Survey on the Physical, Chemical, Thermal, and Mechanical Properties

W4414373951 · 수집 2026-10-04 18:16:39

T10513 Natural Fiber Reinforced Composites

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

The aim of this research is to evaluate the physical, chemical, thermal, and mechanical properties of Itauba (Mezilaurus itauba) wood fiber and Itauba wooden board. The chemical composition presented 33, 29, and 10% lignin, cellulose, and hemicellulose, respectively. The thermal stability was found to be 250 °C for both atmospheres (air and nitrogen), and the simulated TG curve was similar to the one performed on a nitrogen atmosphere. Cone calorimetric results showed a higher steady state when compared to other wood fibers found in the literature with peak heat release rates of 281.762, 424.029, and 482.335 kW/m2 when exposed to constant levels of radiant heat flux of 25, 50, and 75 kW/m2 at similar weights and densities. Furthermore, X-ray diffraction (13.5% crystallinity) and mechanical tests (flexural and tensile Young's modulus of 12010 and 969.9 MPa, respectively) were performed on the Itauba wooden board. The tensile results showed to be higher than propylene composites reinforced with 40% wood fiber found in the literature while the storage modulus obtained in the dynamic mechanical thermal analysis found to be higher (11.5 GPa at -130 °C) than most of the commercial thermoplastics used in the industry (polypropylene (9 × 102 MPa), high-density polyethylene (2 × 103 MPa), and polyvinyl chloride (3000 MPa)). This study showed the potential in using Itauba wooden boards in replacing many commercial products, mainly when an adequate mechanical performance is required.

본문 활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.