Experimental Investigation on the Fatigue Life of Ti-6Al-4V Treated by Vibratory Stress Relief

W2610266096 · 수집 2026-10-04 18:12:31

T11699 High-Velocity Impact and Material Behavior

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Vibratory stress relief (VSR) is a highly efficient and low-energy consumption method to relieve and homogenize residual stresses in materials. Thus, the effect of VSR on the fatigue life should be determined. Standard fatigue specimens are fabricated to investigate the fatigue life of Ti-6Al-4V titanium alloy treated by VSR. The dynamic stresses generated under different VSR amplitudes are measured, and then the relationship between the dynamic stress and vibration amplitude is obtained. Different specimen groups are subjected to VSRs with different amplitudes and annealing treatment with typical process parameters. Residual stresses are measured to evaluate the stress relieving effects. Finally, the fatigue behavior under different states is determined by uniaxial tension–compression fatigue experiments. Results show that VSR and annealing treatment have negative effects on the fatigue life of Ti-6Al-4V. The fatigue life is decreased with the increase in VSR amplitude. When the VSR amplitude is less than 0.1 mm, the decrease in fatigue limit is less than 2%. Compared with specimens without VSR or annealing treatment, the fatigue limit of the specimens treated by VSR with 0.2 mm amplitude and annealing treatment decreases by 10.60% and 8.52%, respectively. Although the stress relieving effect is better, high amplitude VSR will lead to the decrease of Ti-6Al-4V fatigue life due to the defects generated during vibration. Low amplitude VSR can effectively relieve the stress with little decrease in fatigue life.

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-05 11:12:02)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.