The role of initiator on the dispersibility of polystyrene microgels in non-aqueous solvents

W2587736840 · 수집 2026-10-04 18:12:30

T12274 Electrostatics and Colloid Interactions

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Non-aqueous microgel particles are commonly synthesised in water, dried, and then redispersed in non-aqueous solvents. An important factor to consider when synthesising such particles is the initiator, which can determine how well the particles disperse in solvents. Polystyrene microgel particles were made with three different initiators. When a neutral, oil soluble initiator (azobisisobutyronitrile) was used the particles dispersed in toluene as well as cyclohexane and decalin. In contrast, anionic, water-soluble initiators (potassium persulfate or azobis(4-cyanovaleric acid)) created particles that only redispersed in toluene and not the other two solvents. Of the three considered, toluene is the best solvent for polystyrene and also has the highest polarizability, making it most effective at redispersing particles with polar or ionisable functional groups. Zeta potential and conductivity measurements, however, did not detect a direct relationship between particle charging and redispersibility. Oil soluble initiators result in "inside out" polymerisation where the initiator groups are buried inside the growing particle, whereas water-soluble initiators result in "outside in" polymerisation, with the polar initiator groups residing on the particle surface. By tailoring the ratio between water and oil soluble initiators, it may be possible to synthesise microgel particles with uniform or designed charge profiles from the core to the surface.

본문

PDF 본문 자동 추출 실패: [download] not a PDF (Content-Type: text/html, final URL: https://link.springer.com/content/pdf/10.1007/s00396-017-4023-y.pdf) (2026-10-05 09:10:15)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.