IBC c-Si solar cells based on ion-implanted poly-silicon passivating contacts

W2394900147 · 수집 2026-10-04 18:12:25

T10623 Thin-Film Transistor Technologies

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Ion-implanted poly-crystalline silicon (poly-Si), in combination with a tunnel oxide layer, is investigated as a carrier-selective passivating contact in c-Si solar cells based on an interdigitated back contact (IBC) architecture. The optimized poly-Si passivating contacts enable low interface recombination, resulting in implied VOC (iVOC) of about 720 mV and 704 mV for n-type and p-type, respectively, before any hydrogenation step. It is found that high-quality passivation can be obtained when confining the dopants within the poly-Si layers and realizing a shallow diffusion of dopants into the c-Si bulk, meaning a sharp decrease in doping concentration in the c-Si at the poly-Si/c-Si interface. The doping profile at the poly-Si/c-Si interface can be influenced by poly-Si layer thickness, poly-Si ion-implantation parameters, and post-implantation annealing conditions. The detailed discussion on the passivation properties of the poly-Si passivating contacts and their preparation conditions are presented in this paper. In addition, IBC solar cells with/without front surface field (FSF) are fabricated, with the optimized poly-Si passivating contacts as back surface field, BSF (n-type poly-Si), and emitter (p-type poly-Si). The best cell shows an efficiency of 21.2% (VOC=692 mV, JSC=39.2 mA/cm2, FF=78.3%, and pFF=83.5%).

본문

PDF 본문 자동 추출 실패: [download] not a PDF (Content-Type: image/jpeg, final URL: https://ars.els-cdn.com/content/image/1-s2.0-S0927024816301520-fx1_lrg.jpg) (2026-10-05 02:48:39)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.