Thermal Analysis and Flame-Retarded Mechanism of Composites Composed of Ethylene Vinyl Acetate and Layered Double Hydroxides Containing Transition Metals (Mn, Co, Cu, Zn)

W2345835003 · 수집 2026-10-04 18:12:25

T11360 Flame retardant materials and properties

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

The effects of transition metals on the hydrophobicity of nano–structured layered double hydroxides (LDHs) and the compatibility of LDHs/ethylene vinyl acetate (EVA) composites have seldom been reported. NiMgAl–LDHs slightly surface–modified with stearate and doped with transition metal cations (Mn2+, Co2+, Cu2+, Zn2+) are investigated. Compared to the pure EVA, not only were the maximal degradation–rate temperatures (Tmax) of the ethylene–based chains enhanced, but also the smoke production rate (SPR) and the production rate of CO (COP) were sharply decreased for all the composites. Most importantly, a new flame retardant mechanism was found, namely the peak heat release rate (pk-HRR) time, which directly depends on the peak production rate of CO2 (pk-CO2) time for EVA and all composites by cone calorimeter test. Moreover, the Mn–doped LDH S–NiMgAl–Mn shows more uniform dispersion and better interfacial compatibility in the EVA matrix. The cone calorimetric residue of S–NiMgAl–Mn/EVA has the intumescent char layer and the compact metal oxide layer. Therefore, S–NiMgAl–Mn/EVA shows the lowest pk-HRR and the longest pk-HRR time among all the composites.

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-05 02:36:02)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.