Hydrazine solution processed Sb2S3, Sb2Se3 and Sb2(S1−xSex)3 film: molecular precursor identification, film fabrication and band gap tuning

W2265895810 · 수집 2026-10-04 18:12:23

T10321 Quantum Dots Synthesis And Properties

CoT 라벨링

라벨링 전

PDF 파일

자동 다운로드한 PDF PDF 보기

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Abstract Sb 2 (S 1−x Se x ) 3 (0 ≤ x ≤ 1) compounds have been proposed as promising light-absorbing materials for photovoltaic device applications. However, no systematic study on the synthesis and characterization of polycrystalline Sb 2 (S 1−x Se x ) 3 thin films has been reported. Here, using a hydrazine based solution process, single-phase Sb 2 (S 1−x Se x ) 3 films were successfully obtained. Through Raman spectroscopy, we have investigated the dissolution mechanism of Sb in hydrazine: 1) the reaction between Sb and S/Se yields [Sb 4 S 7 ] 2- /[Sb 4 Se 7 ] 2- ions within their respective solutions; 2) in the Sb-S-Se precursor solutions, Sb, S and Se were mixed on a molecular level, facilitating the formation of highly uniform polycrystalline Sb 2 (S 1−x Se x ) 3 thin films at a relatively low temperature. UV-vis-NIR transmission spectroscopy revealed that the band gap of Sb 2 (S 1−x Se x ) 3 alloy films had a quadratical relationship with the Se concentration x and it followed the equation "Equation missing", where the bowing parameter was 0.118 eV. Our study provides a valuable guidance for the adjustment and optimization of the band gap in hydrazine solution processed Sb 2 (S 1−x Se x ) 3 alloy films for the future fabrication of improved photovoltaic devices.

본문

## OPEN

received: 08 January 2015

accepted: 08 May 2015

Published: 04 June 2015

# Hydrazine solution processed Sb2S3, Sb2Se3 and Sb2(S1−xSex)3 film: molecular precursor identification, film fabrication and band gap tuning

Bo Yang 1,2,* , Ding-Jiang Xue 1,2,* , Meiying Leng 1,2 , Jie Zhong 1,2 , Liang Wang 1,2 ,
Huaibing Song 1,2 , Ying Zhou 1,2 & Jiang Tang 1,2

Sb2(S1−xSex)3 (0 ≤ x ≤ 1) compounds have been proposed as promising light-absorbing materials for
photovoltaic device applications. However, no systematic study on the synthesis and characterization
of polycrystalline Sb2(S1−xSex)3 thin films has been reported. Here, using a hydrazine based solution
process, single-phase Sb2(S1−xSex)3 films were successfully obtained. Through Raman spectroscopy,
we have investigated the dissolution mechanism of Sb in hydrazine: 1) the reaction between Sb and
S/Se yields [Sb4S7] 2- /[Sb4Se7] 2- ions within their respective solutions; 2) in the Sb-S-Se precursor
solutions, Sb, S, and Se were mixed on a molecular level, facilitating the formation of highly uniform
polycrystalline Sb2(S1−xSex)3 thin films at a relatively low temperature. UV-vis-NIR transmission
spectroscopy revealed that the band gap of Sb2(S1−xSex)3 alloy films had a quadratical relationship
with the Se concentration x and it followed the equation Eg ( x ) = 0. 118 x 2 - 0. 662 x + 1. 621 eV,

where the bowing parameter was 0.118 eV. Our study provides a valuable guidance for the
adjustment and optimization of the band gap in hydrazine solution processed Sb2(S1−xSex)3 alloy
films for the future fabrication of improved photovoltaic devices.

Recently, antimony selenide (antimonselite, Sb2Se3) has been intensively explored as a light-absorbing
material for photovoltaic device applications, owing to its simple, low-cost and non-toxic composition,
suitable band gap (approximately 1.1 eV) and high optical absorption coefficient of above 10 5 cm −1 at
short wavelength 1–5 . Within one year, solution processed Sb2Se3 sensitized solar cells fabricated using a
single-source precursor have obtained a power-conversion efficiency (PCE) of 3.21% by Seok’s group 3,
and superstrate Sb2Se3 solar cells fabricated via thermal evaporation have achieved 3.7% device efficiency
by our group 6, suggesting the promise of Sb2Se3 for photovoltaic absorber application.

From a device perspective, it would be desirable to introduce S into the Sb2Se3 absorber film forming
alloyed Sb2(S1-xSex)3 (0 ≤ x ≤ 1) film, which could have compositon-dependent properties such as band
gap and band position tunability, similar to the Ga alloying in CuInSe2 thin film solar cells 7 . In such a
way, optimal band alignment and back field grading could be realized, enabling better device performance 8 . Unfortunately, alloyed Sb2(S1-xSex)3 (0 ≤ x ≤ 1) compunds are rarely explored thus far except the
following two examples: in 2008, El-Sayad _et al._ reported amorphous Sb2(S1-xSex)3 (x = 0, 1/3, 2/3, and 1)
films via thermal evaportion 9 ; and in 2009, Deng _et al_ . presented the synthesis of Sb2(S1-xSex)3 (0 ≤ x ≤ 1)
nanotubes via colloidal synthetic method 10 . To our best knowledge, detailed study of the synthesis and

1Wuhan National Laboratory for Optoelectronics (WNLO). 2School of Optical and Electronic Information, Huazhong
University of Science and Technology (HUST), Wuhan, 430074, China. * These authors contributed equally to this
[work. Correspondence and requests for materials should be addressed to J.T. (email: jtang@mail.hust.edu.cn)](mailto:jtang@mail.hust.edu.cn)

characterization of polycrystalline Sb2(S1-xSex)3 (0 ≤ x ≤ 1) thin films, which is most relevant to photovoltaic application, is missing in the literature.

In this report, we have prepared polycrystalline Sb2(S1-xSex)3 (0 ≤ x ≤ 1) films using hydrazine solution
processing. As previously reported, hydrazine is known as a powerful solvent to dissolve many metals
in the presence of excess chalcogens without introducing extra C and O impurities 11–13 . After annealing,
hydrazine and excess chalcogens are removed, leaving behind a polycrystalline metal chalcogenide film
suitable for optoelectronic device applications 14 . For example, ultrathin SnSxSe2-x films with mobility
greater than 10 cm 2 V −1 s −1 and the current champion 12.6% CZTSSe solar cell were all obtained through
the hydrazine solution processing 15,16 . Furthermore, the composition of final film could be simply tuned
by varying S and Se loading in the precursor solution, facilitating the fabrication of Sb2(S1-xSex)3 films with
continuously tunable constituents, in analogy to the hydrazine solution processed CuIn(Se,S)2 films 17 .

Precise composition control over the Sb2(S1−xSex)3 thin films requires a deep understanding of the
mechanism of sulfur incorporation into final Sb2(S1-xSex)3 thin films. We thus first investigated the molecular species present in hydrazine-based Sb-Se, Sb-S, and Sb-S-Se solutions through Raman spectroscopy
which has been proven as an effective tool in the study of hydrazine-based systems previously 18 . This
characterization technique offers the unique opportunity to simultaneously probe the vibrational modes
of a variety of solvated species, and consequently, we successfully uncovered the incorporation mechanism of sulfur into the Sb2(S1-xSex)3 thin films. Through careful X-ray diffraction (XRD), energy dispersive spectroscopy (EDS) and UV-vis-NIR transmission spectroscopy, direct correlation between band
gap and composition of Sb2(S1-xSex)3 thin films across the entire compositional range from x = 0 to 1 was
obtained, yielding a bowing factor of 0.118 eV. Our study not only presented a detailed chemistry picture
of Sb dissovling into hydrazine, but also provided a reliable solution to conveniently tune the band gap of
Sb2(S1-xSex)3 thin films, which should find their application for antimony chalcogenide based solar cells.

Methods
Chemicals. Antimony powder (Sb, 99.999%), elemental sulfur (S, 99.999%), elemental selenium (Se,
99.999%), Sb2S3 powder (99.999%) and Sb2Se3 powder (99.999%) were all purchased from Alfa Aesar.
Anhydrous hydrazine (N2H4, 98%) was purchased from Sinopharm Group Co. Ltd. All chemicals were
used without any purification.

Preparation of precursor solutions. All experiments were done inside a nitrogen filled glovebox
(oxygen and water concentration maintained below 1 ppm). _Caution! Hydrazine is highly toxic and should_
_be handled in the glove box with protective equipment_ 19,20 . In order to prepare the Sb-S solutions with
controlled S/Sb molar ratios ranging from 3.5 to 8, 4 mmol (0.487 g) of Sb powder combined with an
appropriate amount of S were added into 2 mL hydrazine. Similarly, the Sb-Se solutions were prepared
by dissolving 4 mmol of Sb powder combined with an appropriate amount of Se into 2 mL hydrazine
with controlled Se/Sb molar ratios ranging from 3.5 to 6. Pure S or Se stock solution was prepared by
dissolving 32 mmol elemental S or Se powder into 16 mL hydrazine and the S-Se stock solution was prepared by mixing the desired volumes of S solution and Se solution. To prepare Sb2(S1-xSex)3 thin films,
the Sb-S-Se precursor solutions were prepared by adding appropriate volumes of Se stock solution into
2 mL Sb-S solution with S/Sb molar ratio fixed as 3 and Se/(S+Se) molar ratios varied between 0.05, 0.17,
0.27 and 0.38. For example, to yield a Se/(S+Se) molar ratio equaling to 0.05 in the Sb-S-Se precursor
solution, 0.3 mL Se solution (0.6 mmol Se) was added into 2 mL Sb-S solution (4 mmol Sb and 12 mmol
S). Before characterization and thin film deposition, all of solutions mentioned above must be stirred for
a few days until turned into homogeneous solutions with some viscosity.

Film deposition. The Sb2(S1−xSex)3 thin films were deposited by spin-coating Sb-S-Se precursor solutions onto 2.5 × 2.5 cm 2 TiO2 substrates (the preparation method of TiO2 substrates has been described
in detail elsewhere 4,21 ). We used TiO2 substrates because of their better wettability than quartz, soda-lime
glass and silicon wafer in this hydrazine-based solution process.

The Sb-S-Se precursor solutions were filtered through a 0.2 μ m PTFE filter and flooded onto the
substrates, then spun at 400 rpm for 10 s, followed by 2100 rpm for 45 s. After spin-coating, the films
were dried on a preheated hot plate at 100 °C for 10 min, and subsequently annealed at 300 °C for 8 min.

Materials characterization. Raman analysis was performed on the hydrazine precursor solutions
including Sb-S, Sb-Se, Sb-S-Se and S-Se solutions in a backscattering confocal configuration at room
temperature. A LabRAM in Via Raman system was applied for measurement, and the unpolarized light
was generated through a 532 nm Ar laser with power adjusted to 50 mW. Prior to measurement, each
solution was sealed in a glass vial by parafilm in order to minimize oxygen and moisture exposure. X-ray
diffraction (XRD) characterization (Philips, X pert pro MRD, with Cu Kα radiation, λ = 1.54178 Å) was
performed on the annealed Sb2(S1-xSex)3 thin films prepared on TiO2 substrates. The compositions of
the thin films were obtained through energy dispersive spectroscopy (FEI Quanta 600 scanning electron microscope, 20 kV). Sb2S3 powder (99.999%, Alfa Aesar) and Sb2Se3 powder (99.999%, Alfa Aesar)
were used as standards for the calibration of EDS measurements. Scanning electron microscopy (FEI
Nova NanoSEM450, without Pt coating) and UV-vis-NIR transmission spectroscopy (Perkin Elmer

Figure 1. Raman spectroscopy characterization of Sb-S precursor solutions with varied S/Sb ratios. A ) a
digital picture of the Sb-S precursor solutions with varied S/Sb ratios (values marked on the vial). B ) Multipeak fitting of the Raman peaks obtained from the Sb-S precursor solution with an S/Sb molar ratio of 3.5.
C ) Raman spectra of Sb-S precursor solutions with different S/Sb molar ratios from 3.5 to 8. The insert was
the magnified spectra of the S-H peaks at 2560 cm −1 . D ) The integrated intensities of the peaks for the Sb-S
complex (•), and the S-H bond (■) as a function of the S/Sb molar ratio.

Instruments, Lambda 950 using integrating sphere) was performed on the Sb2(S1-xSex)3 films to determine the surface morphology and band gap, respectively.

Results and discussion
Investigation of dissolution mechanism for Sb-X (X = S, Se) hydrazine precursor solutions. We first applied Raman spectroscopy to identify the molecular species presented in the Sb-S
solutions prepared by dissolving Sb powder with elemental S in hydrazine. The picture of these solutions
is shown in Fig. 1A, all of which are clear and transprant. Figure 1B shows the multi-peak fitting for the
Raman spectrum of a 0.5 M Sb-S solution with S/Sb molar ratio of 3.5. Four distinct peaks are visible
at 314, 363, 380 and 2560 cm −1 . The first three peaks are attributable to the symmetric Sb-S stretching
mode which belongs to SbS3 units 22 in the Sb-S complex. The peak located at 2560 cm −1 is the S-H
stretching mode of (N2H5)2S molecules formed by elemental sulfur reacted with hydrazine 23 . Figure 1C
shows the Raman spectra of several Sb-S solutions, prepared with S/Sb molar ratios ranging from 3.5
to 8, and the concentration of Sb was fixed to be 0.5 M. The peaks resulting from Sb-S complex show
negligible changes along with the increase of sulfur concentration; however, the S-H peaks located at
2560 cm −1 show increased amplitude when the S/Sb ratio gradually increased, as evidenced in the insert.
This demonstrates that a certain amount of S react with Sb to form Sb-S complexes, while excess S
form (N2H5)2S molecules in the solution. The intensities of Sb-S and S-H peaks were obtained through
the multi-peak fitting and the corresponding integrated intensities were plotted as a function of the S/
Sb molar ratio, as shown in Fig. 1D. Clearly, the intensity of the Sb-S peaks remained constant versus
different S/Sb ratios, while the intensity of the S-H peaks increased linearly and can be traced back to its
x-intercept at an S/Sb ratio of approximately 1.75. This value represents the critical point at which all of
the dissolved sulfur was completely consumed by reacting with Sb and forming the Sb-S complex. We
thus conclude that the S/Sb ratio of the Sb-S complex is 1.75. Therefore, the simplified chemical formula
of the complex should be [Sb4S7] 2−, which is formed through the following reaction:

8Sb + 14S + 5N 2H4 → 2[Sb4S7]2− + 4N 2H5+ + N 2(gas) (1)

Figure 2. Raman spectroscopy characterization of Sb-Se precursor solutions with varied Se/Sb ratios.
A ) a digital picture of the Sb-Se precursor solutions with varied Se/Sb ratios (value marked on the vial). B )
Multi-peak fitting of the peaks obtained from the Sb-Se precursor solution with a Se/Sb molar ratio of 6. C )
Raman spectra of Sb-Se precursor solutions with Se/Sb molar ratios ranging from 3.5 to 6. D ) The integrated
intensities of the peaks for the Sb-Se complex (•), and the peaks for the Se chain (235 cm −1 ) and Se8 ring
(260 cm −1 ) (■) as a function of the Se/Sb molar ratio.

The formation of [Sb4S7] 2− in the Sb-S hydrazine solution agreed with previous study that [Sb4S7] 2−
ion could steadily exsit in the alkaline aqueous solutions 22,24 .

Following a similar procedure, we have also analyzed the Sb-Se precursor solutions with various Se/
Sb molar ratios, prepared by dissolving Sb powder with elemental Se in hydrazine. The picture of these
solutions is shown in Fig. 2A. Figure 2B shows the multi-peak fitting of the spectrum of a 0.5 M Sb-Se
solution with Se/Sb molar ratio of 6. Three distinct peaks are visible at 216, 235 and 260 cm −1, respectively. The most intense peak, located at 216 cm −1, can be attributed to the pyramidal SbSe3 stretching
mode 25 in the Sb-Se complex. The peak located at 235 cm −1 is assigned to Se-Se vibration in Se chains
while the peak at 260 cm −1 represents symmetric Se-Se stretching mode in the Se8 rings 26,27 . Figure 2C
shows the Raman spectra of several Sb-Se precursor solutions prepared with various Se/Sb molar ratios
between 3.5 and 6. In addition to the peaks corresponding to Sb-Se complex and Se8 ring, some of these
solutions exhibited Raman peaks corresponding to Se chain. Multi-peak fitting for each peak indicates
that the integrated intensities of the peaks corresponding to Se chains and Se8 rings increase apparently
along with the increase of Se content in the Sb-Se solution, while the integrated intensities of the Sb-Se
complex peaks show negligible changes. Clearly, Se reacts with Sb forming Sb-Se complex and the leftover Se forms Se chains and/or Se8 rings in hydrazine. By integrating the intensities of the peaks resulting
from Sb-Se complexes, Se chains and Se8 rings, we plotted the integrated value against the Se/Sb ratio
(Fig. 2D). Obviously, the intensity of the Sb-Se peaks remained constant, while the intensity of the Se
chain and Se8 ring increased linearly, extrapolation of the line to the x-axis produced an intercept of
approximately 1.75, which is equivalently the Se/Sb ratio in the formed Sb-Se complex. Therefore, the
simplified composition of Sb-Se complex present in hydrazine solutions must be [Sb4Se7] 2−, produced
from the following equation:

8Sb + 14Se + 5N 2H4 → 2[Sb4Se7]2− + 4N 2H5+ + N 2(gas) (2)

In brief, both S and Se react with Sb in hydrazine forming [Sb4S7] 2− and [Sb4Se7] 2− complexes.

Preparation of Sb2(S1-xSex)3 thin films. To tune the bandgap of the hydrazine processed Sb2(S1-xSex)3
thin films, we tried to incorporate different amount of S into the final films. We prepared the precursor

Target composition
Sb2(S1-xSex ) 3

Precursor composition (Sb/S/Se

atom ratio %)

Composition measured

by EDS a (Sb/S/Se atom

ratio %) Alloy film stoichiometry Eg (eV) b

Sb2S3 25:75:0 (2:6:0) 39.14:60.86:0 Sb1.96S3.04 (x = 0) 1.62

Sb2(S0.95Se0.05)3 24.1:72.29:3.61 (2:6:0.31) 38.24:53.11:8.65 Sb1.91S2.66Se0.43(x = 0.14) 1.53

Sb2(S0.83Se0.17)3 21.74:65.22:13.02 (2:6:1.2) 39.65:40.43:19.92 Sb1.98S2.02Se1(x = 0.33) 1.42

Sb2(S0.73Se0.27)3 19.51:58.54:21.95 (2:6:2.25) 42.21:28.32:29.47 Sb2.12S1.42Se1.46(x = 0.51) 1.31

Sb2(S0.62Se0.38)3 17.24:51.72:31.04 (2:6:3.6) 42.28:17.32:40.39 Sb2.12S0.86Se2.02(x = 0.70) 1.21

Sb2(S0.50Se0.50)3 25:37.5:37.5 (2:3:3) 38.34:9.48:52.18 Sb1.92S0.47Se2.61(x = 0.85) 1.20

Sb2(S0.33Se0.67)3 25:25:50 (2:2:4) 39.1:2.52:58.38 Sb1.96S0.13Se2.91(x = 0.96) 1.11

Sb2(S0.17Se0.83)3 25:12.5:62.5 (2:1:5) 41.24:0.59:58.17 Sb2.01S0.03Se2.96(x = 0.99) 1.12

Sb2Se3 (x = 1) 25:0:75 (2:0:6) 39.20:0:60.80 Sb1.96Se3.044(x = 1) 1.08

Table 1. Results summary for the composition and optical band gap energies of hydrazine processed
Sb2(S1-xSex)3 films. a EDS measurements have an error which represents the uncertainty of the instrument
measurements. b Optical band gap energies (Eg) were determined from UV-vis-NIR spectra.

Figure 3. Raman spectra of Sb-S-Se precursor solutions and S0.73Se0.27 solution. A ) Sb-S-Se precursor
solutions containing different Se/(Se+S) molar ratios (0.05, 0.17, 0.27 and 0.38). The insert was the
magnified spectra of the peaks located between 200 and 240 cm −1, B) S0.73Se0.27 solution.

solutions by mixing the Sb powder, elemental S and Se altogether in hydrazine. Using a spin-coating
then annealing process carried out inside the glovebox, we successfully produced the Sb2(S1-xSex)3
(0.85 ≤ x ≤ 1) thin films (please refer to the EDS, XRD, and UV-vis-NIR transmission analysis shown
in Table 1, Figure S1, and Figure S2, respectively). The general observation is that the incorporation
efficiency of sulfur into the final films was very low following this strategy. For example, only when 50%
sulfur was included into the precursor solution could we obtain a final Sb2(S0.15Se0.85)3 film containing
15% sulfur. Meanwhile, we tried to add more S into precursor solutions to increase the S content of final
films, which was unfortunately failed due to the insolubility of the solutions. Therefore, we have to find
other methods to increase the incorporation efficiency of sulfur into the final films.

In order to incorporate more S into the final Sb2(S1-xSex)3 films, we prepared Sb-S-Se precursor solutions by adding appropriate volumes of Se stock solution into 2 mL Sb-S precursor solution prepared in
advance. The preparation details were described in the experimental section. To explore the interactions
between Se atoms and [Sb4S7] 2− complex in solution, we applied Raman spectroscopy on the Sb-S-Se
solutions, which were prepared with Se/(Se+S) molar ratios ranging between 0.05 and 0.38 and stirred
for at least one day before Raman characterization. As shown in Fig. 3A, the peaks located at 216 cm −1,
235 cm −1, 260 cm −1, and 363 cm −1 are attributed to [Sb4Se7] 2−, Se chains, Se8 rings, and [Sb4S7] 2−, respectively 22,24–27 . However, the molecular species corresponding to the peak at 229 cm −1 was unknown. To
resolve this mystery, we prepared an S-Se precursor solution by mixing a desired volume of S stock solution with Se stock solution, stirred for at least one day and then measured the Raman spectrum. The S-Se
solution showed four distinct peaks (Fig. 3B). Among them, the peaks at 235, 260, and 2560 cm −1 could
be assigned to the previously observed Se chains, Se8 rings, and (N2H5)2S, while the peak at 320 cm −1
was ascribed to S-Se stretching mode 28 . We thus believed that the 229 cm −1 peak observed in the Sb-S-Se
solution was attributed to Sb-S-Se species, which was probably formed by the Se substitution of S in the

[Sb4S7] 2− complexes forming [Sb4S7-xSex] 2− with x values depending on the amount of Se addition to the
solution. Such an anion exchange is expected considering the very similar chemistry between S and Se

Figure 4. Schematic illustration of the preparation scheme of Sb2(S1−xSex)3 thin films.

Figure 5. Phase characterization of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films with different Se concentration.
A ) XRD patterns of the Sb2(S1-xSex)3 alloy films with their Se concentration in the Sb-S-Se precursor
solutions indicated; B ) enlarged (020) and (120) XRD peaks of the same films as in panel A.

and the unchanged complex configuration after the reaction. This result was further strengthened by
comparing the intensities of [Sb4S7] 2− with [Sb4Se7] 2− and [Sb4S7-xSex] 2− in the Raman spectra. It is clear
that the intensities of [Sb4Se7] 2− and [Sb4S7-xSex] 2− peaks increase apparently along with the increase of
Se content in the precursor solutions, while the intensity of [Sb4S7] 2− peaks gradually weakens. What is
more, mixing Sb, S and Se atoms on a molecular level in the precursor solution facilitates the easy incorporation of S into the final films forming a homogeneous Sb2(S1-xSex)3 alloy phase, a huge advantage for
our study of alloyed Sb2(S1-xSex)3 films.

Figure 4 shows the overall preparation scheme of Sb2(S1-xSex)3 thin films. It should be noted that we
employed elemental Sb, S and Se instead of conventional metal chalcogenide 29,30 to eliminate possible
material composition variation from batch to batch and hence ensure precise composition control in
the final film. Deposition of Sb2(S1-xSex)3 films involved four steps: (i) dissolve Sb with S in hydrazine
to produce the Sb-S stock solution and dissolve Se in hydrazine to produce Se stock solution at room
temperature; (ii) prepare the Sb-S-Se precursor solutions by mixing the Sb-S solution with different volumes of Se solutions, followed by stirring for at least 2 h before spin-coating; (iii) spin-coat the Sb-S-Se
solutions onto prepared TiO2 substrates and (iv) anneal the as-deposited films at 300 °C for 8 min to yield
the Sb2(S1-xSex)3 thin films. In addition, the binary Sb2S3 and Sb2Se3 films were also prepared using the
Sb-S (S/Sb = 3) and Sb-Se (Se/Sb = 3) solutions with the same annealing process.

Se content (x) in the Sb2(S1-xSex)3 films could be tuned across the entire range from 0 to 1 by varying
the volumes of Se stock solution added into Sb-S solution. X-ray diffraction (XRD) was employed to
characterize the formation of Sb2(S1-xSex)3 alloy phase. Figure 5A shows the XRD patterns of six different
Sb2(S1-xSex)3 films produced using Sb-S-Se precursor solutions with Se/S+Se molar ratios of 1, 0.38, 0.27,
0.17, 0.05, and 0, respectively. The variation of the Se/(S+Se) ratio in the Sb2(S1-xSex)3 films is clearly
reflected from the XRD patterns. At x = 1, the XRD pattern corresponds to orthorombic Sb2Se3 (JCPDS
no. 15-0861). As the sulfur concentration increases (that is, x decreases), the diffraction peaks gradually
shift to larger 2θ angle which is clearly visible in the magnified view of (020) and (120) XRD peaks shown
in Fig. 5B. Such a shift to higher angles is attributed to the drcreased lattice constants of the films with

Figure 6. Morphology and composition characterization of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films with
different Se concentration. ( A-I ) Top view SEM images of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films marked
with their Se concentration x of 1, 0.99, 0.96, 0.85, 0.70, 0.51, 0.33, 0.14, and 0, respectively. Insets show the
enlarged images of the corresponding alloy films. ( J ) EDS patterns of Sb2(S1-xSex)3 (0 ≤ x ≤ 1) alloy films; Ti
and Sn signals are from TiO2 and FTO substrates, respectively. ( K ) Plot of Se concerntration x in the final
films calculated from the EDS spectra versus Se concentration in the Sb-S-Se precursor solutions; similarly, S
concerntration 1-x in the final films calculated from from the EDS spectra plotted versus the S concentration
in Sb-S-Se precursor solutions. The error bars represent the uncertainties of the instrument measurements.

gradul substitution of larger Se atoms (1.98 Å) with smaller S atoms (1.84 Å). At x = 0, the XRD pattern
could be well indexed to orthorombic Sb2S3 (JCPDS no. 06-0474). It should be emphasized that none
of our samples have any peaks corresponding to other phases (except from the peaks of FTO substrate
labelled with ▼), indicating that these samples are single-phase, forming the Sb2(S1−xSex)3 alloy films.

Scanning electron microscopy (SEM) was applied to characterize the morphologies of Sb2(S1−xSex)3
films (Fig. 6A–I) marked with Se concentration _x_ of 1, 0.99, 0.96, 0.85, 0.70, 0.51, 0.33, 0.14, and 0,
respectively. The high magnification SEM images shown in the insets indicated that the grain size of
Sb2(S1−xSex)3 thin films varied from 200 to 900 nm. Apparently, more cracks and pinholes appeared in

Figure 7. Optical properties of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films with different Se concentration. A )
UV-vis-NIR transmission spectra of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films; B ) Pots of ( _αhv_ ) 2 vs the photon
energy ( _hv_ ) reveal the band-gaps of Sb2(S1−xSex)3 alloy films as 1.08, 1.21, 1.31, 1.42, 1.53, and 1.62 eV for
x = 1, 0.70, 0.51, 0.33, 0.14, and 0, respectively; C ) Lattice constants a (blue), b (red), and c (green), derived
from XRD diffraction peaks, plotted as functions of Se concentration x in the Sb2(S1-xSex)3 alloy films. The
inserted table shows the comparison of x derived from XRD and EDS. D ) The band gap energy plotted
verus the Se concentration x in the Sb2(S1-xSex)3 alloy films. The solid curve is a quadratic fit to the measured
values of the band gap energy. The error bars labled by the red and green colors represent the uncertainties
in the determination of the composition and the optical band gap of alloy films, respectively.

the final films as the sulfur content increased in the Sb2(S1−xSex)3 alloy films, which may result from the
easier volatilization of sulfur and hence larger volume shrinkage and more violent volume change during
the annealing of Sb2(S1−xSex)3 films. The chemical compositions of Sb2(S1−xSex)3 films were analyzed by
EDS as shown in Fig. 6J. A quantitative elemental EDS analysis of these films revealed that the measured
Se concentration x for each sample was 1.0, 0.99, 0.96, 0.85, 0.70, 0.51, 0.33, 0.14, and 0, which were listed
in Table 1. It should be noted that our EDS facility was calibrated using commericial Sb2S3 and Sb2Se3
powder (Alfa Aesar, 99.999% pure) in advance; and for the composition calculation, EDS results from
three arbitrarily selected spots of each sample were averaged to obtain the final results. The relationship
between the Se or S content in the precursor solutions and those in Sb2(S1−xSex)3 films gave a non-linear
trend, as shown in Fig. 6K. For Se, the content in Sb2(S1−xSex)3 films showed first a superlinearly and
then a slowly increasing trend with increased Se content in the precursor solutions, and the demarcation point was 0.5. On the contrary, S content in the resulting Sb2(S1−xSex)3 films showed first a slowly
(sub-linear) followed by a linearly increasing trend with increased S content in the precursor solutions,
and the demarcation point was 0.5 as well. Clearly, Se was more competitive in being incoporated into
the Sb2(S1−xSex)3 films than S. In brief, with the goal to increase the S content of the final films, the
approach of adding Se solution into Sb-S solution was more effective than that of mixing the Sb powder,
elemental S and Se altogether in hydrazine.

Analysis of optical transmission spectra is one of the most effective tools for understanding the band
structure and energy gaps of semiconductor materials. As shown in the Fig. 7A, optical transmission
spectra of the Sb2(S1-xSex)3 films exhibite a gradual red shift toward longer wavelength with increased Se
composition, which is due to a narrower band gap of Sb2Se3 (~1.08 eV) than that of Sb2S3 (~1.62 eV). For
semiconductors, the optical absorption near band edge follows the formula: (α hν ) n = A n (hν− Eg), where
A is a constant, h is the Planck’s constant, ν is the frequency of the incident photon, Eg is the band gap
and n equals to 2 for direct band gap semiconductors and to 1/2 for an indirect band gap semiconductor 31 . Although the optical transition type of Sb2Se3 and Sb2S3 was still controversial 32, analysis assuming
direct band gap yielded a high quality fitting ((α hν ) 2 versus the photon energy (hν ), Fig. 7B) while
fitting assuming indrect band gap failed. The estimated mean band gaps for our samples were found

to be Eg = 1.62, 1.53, 1.42, 1.31, 1.21, and 1.08 eV, as listed in Table 1. The Eg was thus seen to increase
from 1.08 eV for Sb2Se3 to 1.62 eV for Sb2S3 as the concentration of S increases in the Sb2(S1-xSex)3 series.

For verifying the composition more precisely, we also determined the Se concentration using XRD
patterns. Figure 7C shows the lattice parameters of a, b and c, determined from XRD 33 (a, b and c are
derived from the (200), (020) and (221) peaks respectively), plotted as a function of the Se concentration x in the Sb2(S1−xSex)3 alloy films. The Se concentration x was determined by averaging the values
obtained from calibrated and repeated EDS measurements (first calibrated the system using commercial
99.999% Sb2S3 and Sb2Se3 powder and then measured the EDS value over 6 arbitrarily selected points in
two rounds). As the figure shows, the experimentally measured a, b and c values could be well fitted by
a straight line, which indicated that the dependence of lattice parameters on alloy composition conforms
with the Vegard’s law approximation 34 :

_m_ ( _x_ ) = _x_ × _m_ ( _Sb_ 2 _Se_ 3) + (1       - _x_ ) × _m_ ( _Sb_ 2 _S_ 3) (3)

where _x_, m( _x_ ), m(Sb2Se3) and m(Sb2S3) are the respective Se concentration, lattice parameters _a_, _b_, and _c_
of these orthorhombic structured samples. According to formula (3), the Se concentration _x_ was determined, as listed in the inserted table, which is very close to the results obtained from EDS, further confirming the composition of the alloyed Sb2(S1−xSex)3 films. To further understand the relation between
the alloy composition and their band gap evolution, Fig. 7D plots the band gap of Sb2(S1−xSex)3 films as
a function of Se concentration x. The band gap was also obtained by multi-measurements on different
films. It is found that the optical band gap of alloy samples shows a curve, which is termed as band gap
“bowing” 35 . The data points are fitted by the modified bowing equation as follows:

E _g_ (x) = xESbg 2Se3 + (1−)x _E_ gSb2S3 −(x 1−)x b (4)

2Se3 + (1−)x _E_ Sb2S3

where ESbg 2Se3 and ESbg 2S3 are band gap energies of pure Sb2Se3 and Sb2S3, respectively; b is the bowing

parameter describing the nonlinear relationship between band gap and Se concentration x. Through
fitting by the quadratic equation mentioned above, the dependence of the optical band gap on Se concentration x is characterized by the following relation:

Eg (x) = 0. 118x 2 −.0 662x + 1. 621eV (5)

The bowing parameter of Sb2(S1-xSex)3 alloy films is determined as 0.118 eV. Such a nonlinear dependence of band gap on Se concentration x could possibly arise from three souces: (i) the change of band
structure due to lattice constant variation, (ii) electron distribution deformation due to electronegativity
differences of the alloy atoms, and (iii) relaxation of anion-cation bond lengths and angles 36,37 . Recent
reports of amorphous thin films of Sb2(S1−xSex)3 (x = 0, 1/3, 2/3, and 1) solid solutions 9 and Sb2(S1-xSex)3
(0 ≤ x ≤ 1) nanotubes 10 indicate quadratically increasing optical band gap energy with sulfur content,
which is in good agreement with our findings. The bowing parameter “b” reported in these two papers
are 0.02 and 0.03 eV, respectively, which are smaller than our 0.118 eV. This may results from the difference of preparation process. On account of the extremely careful composition (EDS and XRD) and band
gap measurements, we believe that our results are credible for polycrystalline Sb2(S1−xSex)3 (0 ≤ x ≤ 1)
alloy films, which is more relevant for photovoltaic application. We summarize our experimental results
on the composition and band gap study of hydrazine solution processed Sb2(S1−xSex)3 films in Table 1.

Conclusions
In summary, we have systematically studied the dissolution mechanism of Sb in hydrazine, and the
composition dependent band gap of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films. The major findings are: 1) Sb
reacts with S and Se in hydrazine forming (N2H5)2Sb4S7 and (N2H5)2Sb4Se7 molecules producing clear
solutions; 2) mixing of Se hydrazine solution with Sb-S hydrazine solution leads to anion mixing on a
molecular level, facilitating production of highly uniform polycrystalline Sb2(S1−xSex)3 thin films at a
relatively low temperature; 3) for Sb2(S1−xSex)3 alloy films, the XRD peaks’ position dependence on composition is linear while the the band gap dependence on composition is quadratical and it follows the
equation Eg (x) = 0. 118x 2 −.0 662x + 1. 621eV, where the bowing parameter is 0.118 eV. Our study

provide a valuable guidance for the band gap tunning of Sb2(S1−xSex)3 (0 ≤ x ≤ 1) alloy films, which
should find their application for antimony chalcogenide based solar cells.

References

1. Chang, J. A. _et al._ High-performance nanostructured inorganic-organic heterojunction solar cells. _Nano Lett._ 10, 2609–2612
(2010).
2. Im, S. H. _et al._ Toward interaction of sensitizer and functional moieties in hole-transporting materials for efficient semiconductorsensitized solar cells. _Nano Lett._ 11, 4789–4793 (2011).
3. Choi, Y. C. _et al._ Sb2Se3-sensitized inorganic-organic heterojunction solar cells fabricated using a single-source precursor.
_Angewandte Chemie_ 126, 1353–1357 (2014).
4. Zhou, Y. _et al._ Solution-processed antimony selenide heterojunction solar cells. _Adv_ . _Energy Mater._ 4, DOI: 10.1002/
aenm.201301846 (2014).

5. Liu, X. _et al._ Thermal evaporation and characterization of Sb2Se3 thin film for substrate Sb2Se3/CdS solar cells. _Acs Appl. Mater._
_Interfaces_ 6, 10687–10695 (2014).
6. Leng, M. _et al._ Selenization of Sb2Se3 absorber layer: An efficient step to improve device performance of CdS/Sb2Se3 solar cells.
_Appl. Phys. Lett._ 105, 083905 (2014).
7. Turcu, M. & Rau, U. Compositional trends of defect energies, band alignments, and recombination mechanisms in the Cu(In,
Ga)(Se, S)2 alloy system. _Thin Solid Films_ 431, 158–62 (2003).
8. Choi, Y. C. _et al._ Efficient inorganic-organic heterojunction solar cells employing Sb2(Sx/Se1-x)3 graded-composition sensitizers.
_Adv. Energy Mater._ 4, DOI: 10.1002/aenm.201301680 (2014).
9. El-Sayad, E. Compositional dependence of the optical properties of amorphous Sb2Se3−xSxthin films. _J. Non-cryst. Solids._ 354,
3806–3811 (2008).
10. Deng, Z., Mansuripur, M. & Muscat, A. J. Simple colloidal synthesis of single-crystal Sb-Se-S nanotubes with composition
dependent band-gap energy in the near-infrared. _Nano Lett._ 9, 2015–2020 (2009).
11. Mitzi, D. B. Solution processing of chalcogenide semiconductors via dimensional reduction. _Adv. Mater._ 21, 3141–3158 (2009).
12. Zhong, J. _et al._ Sulfurization induced surface constitution and its correlation to the performance of solution-processed Cu2ZnSn(S,
Se)4 solar cells. _Sci. Rep_ . 4 (2014).
13. Yang, B. _et al._ CuSbS2 as a promising earth-abundant photovoltaic absorber material: a combined theoretical and experimental
study. _Chem. Mater._ 26, 3135–3143 (2014).
14. Yang, W. _et al._ Novel solution processing of high-efficiency earth-abundant Cu2ZnSn(S, Se)4 solar cells. _Adv. Mater._ 24, 6323–
6329 (2012).
15. Mitzi, D. B., Kosbar, L. L., Murray, C. E., Copel, M. & Afzali, A. High-mobility ultrathin semiconducting films prepared by spin
coating. _Nature_ 428, 299–303 (2004).
16. Wang, W. _et al._ Device characteristics of CZTSSe thin-film solar cells with 12.6% efficiency. _Adv. Energy Mater._ 4, DOI:10.1002/
aenm.201301465 (2014).
17. Chung, C.-H. _et al._ Mechanism of sulfur incorporation into solution processed CuIn(Se,S)2 films. _Chem. Mater._ 23, 4941–4946
(2011).
18. Ziomek, J. S. & Zeidler, M. D. Raman spectra, normal coordinate treatment, and calculated thermodynamic properties for
hydrazine and tetradeuterohydrazine. _J. Mol. Spectrosc._ 11, 163–184 (1963).
19. Sotaniemi E, J. H., Isom-aki, H., Takkunen, J. & Kaila, J. _Ann.Clin. Res._ 3, 30 (1971).
20. Audrieth, L. F. & Ogg, B. A. _The chemistry of hydrazine_ . (Wiley, New York, 1951).
21. Liu, H. _et al._ Electron acceptor materials engineering in colloidal quantum dot solar cells. _Adv. Mater._ 23, 3832–3837 (2011).
22. Wood, S. A. Raman spectroscopic determination of the speciation of ore metals in hydrothermal solutions: I. Speciation of
antimony in alkaline sulfide solutions at 25 C. _Geochim. Cosmochim. Ac_ 53, 237–244 (1989).
23. Chung, C.-H. _et al._ Identification of the molecular precursors for hydrazine solution processed CuIn(Se, S)2 films and their
interactions. _Chem. Mater._ 23, 964–969 (2011).
24. Arntson, R., Dickson, F. & Tunell, G. Stibnite (Sb2S3) solubility in sodium sulfide solutions. _Science_ 153, 1673–1674 (1966).
25. Adam, A. B. Infrared and Raman studies on Snx–Sb5–Se95−x chalcogenide glasses. _Journal of King Saud University-Science_ 21,
93–97 (2009).
26. Yannopoulos, S. N. & Andrikopoulos, K. S. Raman scattering study on structural and dynamical features of noncrystalline
selenium. _J. Chem. Phys._ 121, 4747–4758 (2004).
27. Nagata, K., Ishikawa, T. & Miyamoto, Y. Raman spectrum of selenium dissolved in an aqueous solution of sodium sulfide. _Jpn._
_J. Appl. Phys._ 24, 1171 (1985).
28. Ishii, M., Shibata, K. & Nozaki, H. Anion distributions and phase transitions in CuS1-xSex (x = 0-1) studied by Raman spectroscopy.
_J. Solid State Chem._ 105, 504–511 (1993).
29. Yuan, M. & Mitzi, D. B. Solvent properties of hydrazine in the preparation of metal chalcogenide bulk materials and films.
_Dalton. Trans._, 6078–6088 (2009).
30. Todorov, T. K., Gunawan, O., Gokmen, T. & Mitzi, D. B. Solution-processed Cu(In, Ga)(S, Se)2 absorber yielding a 15.2% efficient
solar cell. _Prog. Photovoltaics Res. Appl_ . 21, 82–87 (2013).
31. Davis, E. & Mott, N. Conduction in non-crystalline systems V. Conductivity, optical absorption and photoconductivity in
amorphous semiconductors. _Philos. Mag._ 22, 0903–0922 (1970).
32. Vadapoo, R., Krishnan, S., Yilmaz, H. & Marin, C. Electronic structure of antimony selenide (Sb2Se3) from GW calculations.
_Phys. Status Solidi (b)_ 248, 700–705 (2011).
33. Kuykendall, T., Ulrich, P., Aloni, S. & Yang, P. Complete composition tunability of InGaN nanowires using a combinatorial
approach. _Nat. Mater._ 6, 951–956 (2007).
34. Vegard, L. & Schjelderup, H. Constitution of mixed crystals. _Phys. Z_ . 18, 93–96 (1917).
35. Razeghi, M. _Fundamentals of solid state engineering_ . (Springer, Evanston, 2006), 2 edn.
36. Bernard, J. E. & Zunger, A. Electronic structure of ZnS, ZnSe, ZnTe, and their pseudobinary alloys. _Phys. Rev. B_ 36, 3199 (1987).
37. Wei, S.-H., Zhang, S. & Zunger, A. First-principles calculation of band offsets, optical bowings, and defects in CdS, CdSe, CdTe,
and their alloys. _J. Appl. Phys._ 87, 1304–1311 (2000).

Acknowledgments
This work was financially supported by the “National 1000 Young Talents” project, the National
Natural Science Foundation of China (61274055, 61322401, 21403078), the director fund of Wuhan
National Laboratory for Optoelectronics, China Postdoctoral Science Foundation (2013M542015) and
Fundamental Research Funds for the Central Universities, HUST (0118187043, CXY12M008). The
authors thank the Analytical and Testing Center of HUST and the facility support of the Center for
Nanoscale Characterization and Devices, Wuhan National Laboratory for Optoelectronics (WNLO).

Author Contributions
Y.B. and D-J.X. contribute equally to this work, who designed and carried out the major part of the
experiments, analyzed the data and wrote the paper. J.T. designed and supervised whole experimental
processes and wrote the paper. M.L., J.Z., L.W., H.S. and Y.Z. discussed the results and commented on
the manuscript.

Additional Information
Supplementary information [accompanies this paper at http://www.nature.com/srep](http://www.nature.com/srep)

Competing financial interests: The authors declare no competing financial interests.

How to cite this article : Yang, B. _et al._ Hydrazine solution processed Sb2S3, Sb2Se3 and Sb2(S1–xSex)3
film: molecular precursor identification, film fabrication and band gap tuning. _Sci. Rep._ 5, 10978; doi:
10.1038/srep10978 (2015).

This work is licensed under a Creative Commons Attribution 4.0 International License. The
images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the
Creative Commons license, users will need to obtain permission from the license holder to reproduce
[the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/](http://creativecommons.org/licenses/by/4.0/)

본문 출처 PDF: PDF 보기 · 다른 PDF는 위 [PDF 업로드]로 올릴 수 있습니다.

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.