Scalable Fabrication of Natural-Fiber Reinforced Composites with Electromagnetic Interference Shielding Properties by Incorporating Powdered Activated Carbon

W2209478126 · 수집 2026-10-04 18:12:22

T10513 Material Properties and Applications

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Kenaf fiber-polyester composites incorporated with powdered activated carbon (PAC) were prepared using the vacuum-assisted resin transfer molding (VARTM) process. The product demonstrates the electromagnetic interference (EMI) shielding function. The kenaf fibers were retted in a pressured reactor to remove the lignin and extractives in the fiber. The PAC was loaded into the freshly retted fibers in water. The PAC loading effectiveness was determined using the Brunauer-Emmett-Teller (BET) specific surface area analysis. A higher BET value was obtained with a higher PAC loading. The transmission energies of the composites were measured by exposing the samples to the irradiation of electromagnetic waves with a variable frequency from 8 GHz to 12 GHz. As the PAC content increased from 0% to 10.0%, 20.5% and 28.9%, the EMI shielding effectiveness increased from 41.4% to 76.0%, 87.9% and 93.0%, respectively. Additionally, the EMI absorption increased from 21.2% to 31.7%, 44.7% and 64.0%, respectively. The ratio of EMI absorption/shielding of the composite at 28.9% of PAC loading was increased significantly by 37.1% as compared with the control sample. It was indicated that the incorporation of PAC into the composites was very effective for absorbing electromagnetic waves, which resulted in a decrease in secondary electromagnetic pollution.

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-04 23:16:16)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.