Self-Assembly of High Density of Triangular Silver Nanoplate Films Promoted by 3-Aminopropyltrimethoxysilane

W2102969468 · 수집 2026-10-04 18:12:19

T10321 Nanomaterials and Printing Technologies

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

In this work, we studied the structure of synthesized triangular silver nanoplates in solution and the growth of the nanoplates on a silicon surface using 3-aminopropyltrimethoxysilane (APTMS) as a coupling agent. The triangular-shaped colloidal silver nanoplates were simply synthesized by a direct chemical reduction approach. We studied the three characteristic peaks of the unique optical absorbance of triangular silver nanoplates and subsequently measured an average edge length of 26 ± 1 nm. The nanoplate thickness was determined to be 7 ± 2 nm from transmission electron microscopy images. Depositing the nanoplates on a silicon surface was carried out to determine the coverage of triangular nanoplates obtained when adhesion was promoted by a coupling agent. The APTMS film assisted the attachment of the nanoplates to the silicon surface and the coverage of the nanoplates increased with increasing deposition time. The triangular silver nanoplate thin film was a monolayer and a high coverage (near complete) was obtained after eight hours of exposure to the nanoplate solution. The silver film formed was shown to be a good surface-enhanced Raman scattering (SERS) substrate as it gave an enormous Raman enhancement for bisphenol A (BPA).

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-04 22:11:01)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.