Temperature-dependent size effects on the strength of Ta and W micropillars

W2097646372 · 수집 2026-10-04 18:12:19

T10377 Metal and Thin Film Mechanics

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

The strength of metals increases with decreasing sample size, a trend known as the size effect. In particular, focused ion beam-milled body-centered cubic (BCC) micropillars exhibit a size effect known to scale with the ratio of the test temperature to the critical temperature (Tc) of the BCC metal, a measure of how much the yield stress is governed by the lattice resistance. In this paper, this effect is systematically studied by performing high-temperature compression tests on focused ion beam-manufactured Ta and W single crystal pillars ranging in diameter from 500 nm to 5 μm at temperatures up to 400 °C, and discussed in the context of bulk strength and size dependent stresses. Both metals show larger size effects at higher temperatures, reaching values that are in the range of FCC metals at temperatures near Tc. However, it is demonstrated that size effects can be considerably affected by material parameters such as dislocation density and lattice friction, as well as by the yield criterion used. Furthermore, for W, a change from uniform wavy deformation to localized deformation is observed with increasing temperature and pillar size, further indicating that the temperature ratio strongly influences the relative motion of screw and edge dislocations.

본문

PDF 본문 자동 추출 실패: [download] not a PDF (Content-Type: image/jpeg, final URL: https://ars.els-cdn.com/content/image/1-s2.0-S1359645415300173-am12488-ga-5001_lrg.jpg) (2026-10-04 22:08:03)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.