The Use of Le Bail Method to Analyze the Semicrystalline Pattern of a Nanocomposite Based on Polyaniline Emeraldine-Salt Form andα-Al2O3

W2093752495 · 수집 2026-10-04 18:12:19

T10660 Conducting polymers and applications

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Ceramic nanocomposites constituted by a matrix of α -Al 2 O 3 microparticles reinforced by polyaniline emeraldine-salt form (PANI-ES) nanoparticles were prepared by in situ polymerization and characterized structural and morphologically. Peaks related to both materials were observed through XRD technique: PANI-ES presented peaks at<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M1"><mml:mn>2</mml:mn><mml:mi>θ</mml:mi></mml:math>= 8.9, 14.9, 20.8, 25.3, 27.1, and 30.0° and in α -Al 2 O 3 phase peaks were found at<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M2"><mml:mn>2</mml:mn><mml:mi>θ</mml:mi></mml:math>= 25.6, 35.2, 37.9, 43.5, 52.6, 57.6, and 68.1°. Nanocomposite crystallinity percentage was estimated around 70%. SEM showed a polymerization of PANI-ES over alumina plates. By Le Bail method it was observed that PANI-ES and α -Al 2 O 3 have crystallite average size around, respectively, 41 and 250 Å. By FTIR analysis characteristic absorption bands of both materials were identified. Additional bands indicating new chemical bonds were not observed, suggesting that nanocomposite was formed by physical deposition. Nanocomposite DC electrical conductivity was found around 0.24 S/cm (against<mml:math xmlns:mml="http://www.w3.org/1998/Math/MathML" id="M3"><mml:mn>1.84</mml:mn><mml:mo>×</mml:mo><mml:msup><mml:mrow><mml:mn>10</mml:mn></mml:mrow><mml:mrow><mml:mo>-</mml:mo><mml:mn mathvariant="normal">4</mml:mn></mml:mrow></mml:msup></mml:math> S/cm for pure PANI-ES), showing an increase of about 1,300 times compared to the pure PANI-ES at room temperature. Thus, this paper showed that both materials have kept its original structural characteristics and exhibited high electrical conductivity when combined in nanocomposite form.

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-04 22:06:23)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.

The Use of Le Bail Method to Analyze the Semicrystalline Pattern of a Nanocomposite Based on Polyaniline Emeraldine-Salt Form and<i>α</i>-Al<sub>2</sub>O<sub>3</sub>

CoT 라벨링

PDF 파일

이력 0건