Studies on thermal and viscoelastic properties of vinyl ester resin and its composites with glass fiber

W2060257021 · 수집 2026-10-04 18:12:19

T11145 Epoxy Resin Curing Processes

CoT 라벨링

라벨링 전

PDF 파일

자동 다운로드한 PDF PDF 보기

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

Vinyl ester resins are widely used in sandwich composite structures. Because of their good resistance to chemicals, flexibility and easy processing, these sandwich are extensively applied in the marine sector. These composites are typically manufactured by liquid molding processes, especially infusion. In this study, RTM light was used to inject the polymeric resin into the mold cavity, flowing in the space between the impermeable core and the mold walls, where the fibrous medium was. In this process, viscosity, gel time and curing time of the resin are very important parameters. This work addressed the curing and post-curing characteristics of a vinyl ester resin, and also the characteristics of neat and reinforced vinyl ester using dynamic mechanical analysis (DMA). The increase in shear rate did not significantly influence resin viscosity within the studied range. Differential scanning calorimetry showed the efficiency of the post-curing stage, with the decrease in residual enthalpy. With DMA, it was possible to determine gel time and gel temperature, which yielded similar values to those found by the SPI (Society of the Plastics Industry) method, indicating that the simpler SPI method can be reliably used for that.

본문

ISSN 1517-7076 artigo 11577, pp.64-71, 2015

# Studies on thermal and viscoelastic properties of vinyl ester resin and its composites with glass fiber

André C. Garay 1, Lucas T. Paese 1,
Jeferson A. Souza 2, Sandro C. Amico 1

1 GCOMP/LAPOL/PPGEM - UFRGS C.P. 91501-970, Porto Alegre/RS.
e-mail: andrecechin@yahoo.com.br; lucas_paese@hotmail.com; amico@ufrgs.br
2 School of Engineering – FURG C.P. 96203-900, Rio Grande/RS.
e-mail: jasouza@furg.br

ABSTRACT
Vinyl ester resins are widely used in sandwich composite structures. Because of their good resistance to
chemicals, flexibility and easy processing, these sandwich are extensively applied in the marine sector. These
composites are typically manufactured by liquid molding processes, especially infusion. In this study, RTM
light was used to inject the polymeric resin into the mold cavity, flowing in the space between the impermeable core and the mold walls, where the fibrous medium was. In this process, viscosity, gel time and curing
time of the resin are very important parameters. This work addressed the curing and post-curing characteristics of a vinyl ester resin, and also the characteristics of neat and reinforced vinyl ester using dynamic mechanical analysis (DMA). The increase in shear rate did not significantly influence resin viscosity within the
studied range. Differential scanning calorimetry showed the efficiency of the post-curing stage, with the decrease in residual enthalpy. With DMA, it was possible to determine gel time and gel temperature, which
yielded similar values to those found by the SPI (Society of the Plastics Industry) method, indicating that the
simpler SPI method can be reliably used for that.

Keywords: Vinyl ester, DMA, RTM light, sandwich composites.

1. INTRODUÇÃO

Vinyl ester resins (VER) result from the reaction between bisphenol-A based epoxy oligomers and unsaturated carboxylic acids, such as acrylic or methacrylic acid which provides unsaturated terminal sites [1]. This
resin is one of the most important thermoset polymers that combine the chemical, mechanical and thermal
properties of epoxy resins with the fast cure of unsaturated polyester resins (UPRs) [2-3].

Composite materials produced with vinyl ester resins and glass fibers are widely used in marine application, such as fishing trawlers, canoes, patrol boats, mine hunters and submarine domes [4]. In many cases,
sandwich composite structures are chosen and the easy processing of VER allows the use of liquid molding
techniques, such as infusion and RTM light. In these processes, resin is injected into the mold cavity, flowing
in the space between the impermeable core of the sandwich and the mold walls, where the fibrous medium is.
Since resin flow occurs through long distances, viscosity and gel time of the resin become critical parameters.

The cure of VER plays a vital role in their processing and cure kinetics studies have received much
attention. Calorimetry has been used to determine the effect of the initiator concentration and oxygen on the
rate of cure [5]. These resins generally contains 30-60% styrene by weight, which serves as diluents to enhance linear chain extension and to reduce viscosity of the resin, allowing for easy processing and room temperature curing [6]. Styrene also acts as a “bridge’’ between chains during the cross-link process, that occurs
when an initiator opens up double-carbon bonds between vinyl ester and styrene molecules, allowing these
free radicals to link and crosslink, resulting in a cured material with high strength and resistance to degradation.

In fact, viscosity of VER, which varies with their molecular weight, the amount of styrene dissolved
in it and the temperature [1], is a property of fundamental importance when they are used to produce a thermoset composite using any technique of the liquid molding family, such as resin transfer molding (RTM),

Autor Responsável: André Garay Data de envio: 08/01/2013 Data de aceite: 04/11/2014

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

RTM light (L-RTM) [7] and vacuum assisted resin infusion (VARI). These processes are rapidly becoming
very popular because they are ecofriendly, being carried out in closed molds [8].

Dynamic mechanical analysis (DMA) has proven a valuable tool for studying the structure of polymers and composites [8, 9]. Study of the glass transition by DMA involves measuring loss and storage modu-
lus of the material in a given oscillation frequency from room temperature to above the glass transition temperature (Tg). During curing of a thermoset polymer, the number of crosslinks increases, consequently, reducing mobility of the molecular segments and increasing Tg of the material [5]. Once the temperature of the
material exceeds the curing temperature, freezing of the reactive groups occurs, preventing further reactions

[10]. Post-curing of the polymer also modifies loss and storage modulus, and its Tg, that can be used to verify
completeness of the curing reaction.

This work aims to study characteristics of interest of a vinyl ester resin for liquid molding processing,
including viscosity variation with shear rate and temperature, gel time and maximum curing temperature. The
influence of post-curing on the viscoelastic properties (storage modulus, loss modulus and tan δ) of neat and
glass-fiber reinforced resin was also investigated.

2. EXPERIMENTAL

2.1 Materials

Commercial vinyl ester resin (Derakane momentum 470-300) was used. Commercial grade initiator Butanox
M-50 (methyl-ethyl-ketone peroxide, P-MEK), at 1.0-2.0%, catalyzed with 0.6% of cobalt naphthenate
(NafCO), both in relation to the resin volume. E-glass fiber mats (350 g/m2) manufactured by Owens Corning were used as reinforcement.

2.2 Methods

Viscosity measurements were performed with neat resin (without initiator), from 0 to 40 °C. A Brookfield
HBDV-II+C/P viscometer was used with the S51 spindle and at different speeds (20, 30, 50, 60 e 100 rpm).
Gel time and maximum temperature of cure were determined according to the SPI method together with
ASTM D2471. Differential scanning calorimetry (DSC) was carried out in a DSC equipment (model
Q20V24.2 Build107), within 20-250 °C temperature range, under nitrogen atmosphere with a heating rate of
10 °C/min.

Six types of rigid samples were studied: cured and post-cured neat resin, 4-layers cured/post-cured
composite (C4 and C4,pc, respectively), 6-layers cured/post-cured composite (C6 and C6,pc, respectively). The
neat resin samples were cast into silicone molds with rectangular geometry (length × width × thickness: 35 ×
12 × 4 mm). The monolithic composites C4 and C6 were produced by RTM, that comprises the injection of
the liquid resin into a closed mold cavity (320 × 150 × 3.6 mm) containing the fiber reinforcement and the
subsequent resin cure at room temperature for 24 h, producing a rigid composite. Post-curing at 90 °C for 6 h
was done in an air-circulation oven (DLAF02-2).

Fiber volume fraction of the composites was determined using the rule of mixtures and also following
burning in a muffle furnace (at 560 ± 25 °C for 6 h) and weighing of the residue. Resin and composite density were calculated using the Archimedes method. Shore D hardness was performed according to ASTM
D2240-05 in DWOLTEST durometer, model SD300, with 10 measurements in each sample. Dynamic mechanical analysis (DMA) was performed in a TA Instruments Model 2980 (up to 600 ºC), at various frequencies (0.1, 1.0, 3.0, 10, 30 and 100 Hz).

3. RESULTS AND DISCUSSION

Figure 1 shows the variation in resin viscosity with temperature and shear rate. Viscosity of the uncured resin
decreases within the increase in temperature (Figure 1a) due to the gradual weakening of interaction (van der
Waals) forces in the resin. The increase in shear rate did not significantly influence resin viscosity in the
studied range (Figure 1b). A high viscosity is an aggravating factor in liquid molding processes, which would
be prohibitive for usual processing at low temperatures (in this case, 0-15 °C).

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

Figure 1: Variation of resin viscosity with temperature (a) and shear rate with velocity and viscosity in 25 °C (b).

The DSC heat flow curves of the cured and post-cured neat resin are shown in Figure 2a. The cured
resin sample shows a large peak (within ~50-160 °C), with an associated enthalpy of reaction of 327.3 J/g
and a Tg value of ~110 ºC. As for the post-cured resin sample, the measured residual enthalpy (6.9 J/g) was
comparatively negligible, and Tg shifted to ~115 ºC. This decrease in the value of enthalpy due to elimination
of residual reactions, which leaves almost complete reaction.

The tan δ curves obtained with DMA for the cured and post-cured samples are shown in Figure 2b.
The cured sample shows two peaks, at ~65 °C and ~120 °C, similar values to those found in the literature that
were ~68 °C and ~127 °C [4]. The former nearly disappears and the latter narrows and shifts to ~115 °C after
post-curing. The presence of two tan δ peaks can be attributed to the partial cure of the resin, whereas a single peak, i.e. only one glass transition temperature (Tg) [11], suggests the complete cure of the resin, highlighting the need for post-curing. It is therefore interesting to notice that the cured resin shows a shoulder at
around 60-70 o C in both DSC and DMA curves.

With post-curing, residual reactions are almost completely eliminated, avoiding adverse effects on the
mechanical properties. This is ratified by the Shore D hardness values, which increased from 1.55 (± 0.13) to
1.62 (± 0.11) after post-curing of the Resin-1.0% initiator sample due to increased crosslinking, i.e. the material becomes more rigid.

Figure 2: Characteristics of the cured and post-cured (1.0% initiator) samples by: a) DSC and b) DMA (at 3 Hz).

Table 1 compiles the results obtained with the Society of the Plastics Industry (SPI) method for all
samples. Gel time decreased and the maximum curing temperature (Tmax) increased with the increase in initiator content (within 1.0-2.0%). Gel time of a particular resin system is a very important parameter because it
limits the time window for molding. Even though higher initiator content means faster curing, when this level
is above 2.0%, it adversely accelerates the reaction, yielding bubbles (so-called "resin boiling") and preventing complete curing. The variation in gel temperature was a little less pronounced, but also showed an increasing trend for higher P-MEK content.

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

Table 1: Gel time, gel temperature and maximum curing temperature of studied systems.

System Gel time (min) T gel (ºC) T max (ºC)
Resin-1.0% initiator 36.9 93.8 138.4
Resin-1.5% initiator 24.0 106.7 154.8
Resin-2.0% initiator 19.7 104.9 156.5

The tan δ curves obtained by DMA at distinct frequencies for the cured Resin-1% sample are seen in
Figure 3. The E’ (storage modulus) values are smaller than E’’ (loss modulus), knowing that tan δ = E’’/ E’,
confirming that the characteristics of an elastic solid are not reached before the gel region. Increasing the
frequency leads to the increase in storage modulus (i.e. rigidity) and the shift in tan δ to lower temperatures.
It is also seen that there is a shift of Tg to higher temperatures with the increase in frequency. This occurs
because the greater the frequency, the more lagged response of the material when subjected to tension, because the relaxation time is longer. The other samples showed similar behavior.

The gel time of the resin can be determined by the tan δ peak maximum criterion [12]. The gel time
values were within the 32 to 35 min range and the gel temperature within 115-125 °C. These values are close
to those found with the SPI method (Table 1), and the difference may be due to excessive heat loss in the
technique.

Figure 3: Tan δ curve obtained at distinct frequencies for the cured resin-1% sample.

Density and fiber volume fraction of the composites are shown in Table 2. Density increased with fiber content due to the higher density of E-glass in comparison with the VER (2.54 and 1.18 g/cm 3, respectively). The C4 sample, with four layers (%Vf = 16.3-17.0%), is almost at the limit of the so-called structural
composites [13], whereas C6 sample has %Vf = 21.6-23.0%. Fiber content directly influences the thermomechanical properties of the composite.

Table 2: Density and fiber volume fraction of composites C4 and C6.

ρ
Composites
(g/cm 3 )

Vf (Archimedes)

(%)

Vf (Burned)

(%)

C4 1.448 17.0 16.3

C6 1.537 23.0 21.6

The influence of post-curing on the thermo-mechanical properties of vinyl ester composites produced
by RTM was investigated. Variation in storage modulus with temperature for the composites is given in Figures 4-5. Addition of the E-glass fiber reinforcement increases the storage modulus E’ of the resin, that further increases with fiber content e.g. C4 ~4000 MPa and C6 ~6200 MPa for 0.1 Hz, which is due to greater

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

restrictions imposed by the glass fiber to the matrix movement [14]. As the temperature increases, E' decreases, with a sharp decline in the glassy region. This can be attributed to the increased molecular mobility of the
polymer chains above Tg.

In both samples, post-curing increased storage modulus in around 40%, again due to the increase in
the degree of crosslinking which yields a more rigid composite. In addition, the shoulders in the DMA spectra in the viscous region (before Tg) disappeared with the post-curing (e.g. compare Figures 4a-b). The same
was noted in both C4 and C6 composites. The change in DMA spectra endorsed the complete cure of the
composite and the need for post-curing. The effect of frequency variation can be summarized as, at higher
frequencies, the E' values are higher and the composite behaves more like a glassy material (i.e. more rigid)
due to the longer relaxation times in comparison with the timescale of the experiment.

Figure 4: Storage modulus curves of the cured C4 (a) and post-cured C4 (b) composites for different frequencies.

Figure 5: Storage modulus curves of the cured C6 (a) and post-cured C6 (b) composites for different frequencies.

Figures 6-7 shows the variation of loss modulus (E'') as a function of temperature for the composites.
The loss modulus evaluates the energy released by the material during cyclic loading, being mainly influenced by fiber-matrix interaction. The difference with post-curing is clear, and the difference was greater at
the main peaks of the curves for example C4 ~400 MPa and post-cured C4 ~550 MPa for 1.0 Hz (Figure 6).
Here again, it is seen that post-curing eliminated residual effects. For the C6 system, a distinct behavior was
noticed, for example C6 ~590 MPa and post-cured C6 ~520 MPa for 1.0 Hz (Figure 7). Comparing Figures 6
and 7, the loss modulus of C6 was higher than the C4, which was attributed to greater load-transfer for higher
fiber volume fraction. In addition, disappearance of the multiple shoulders in DMA spectra of the composites
after post-curing endorses the final completeness of the curing reached.

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

Figure 6: Loss modulus curves of the C4 (a) and post-cured C4 (b) composites for different frequencies.

Figure 7: Loss modulus curves of the C6 (a) and post-cured C6 (b) composites for different frequencies.

From Figures 8-9, it is clear that there is a shift in Tg to higher temperatures with increasing frequency.
For example, for post-cured C4, the Tg values are 140, 145, 150 and 155 °C, and for post-cured C6, the Tg
values are 130, 135, 145 and 155 °C. This is because the higher the test frequency, the more lagged is the
response of the material subjected to tension, as discussed above. The cured samples show two distinct peaks,
one larger at ~100 °C (C4) or ~90 °C (C6) and another one at ~135 °C (C4) or ~130 °C (C6). The lower temperature peak disappears after post-curing, leaving a single peak. Here again, the presence of two tan δ peaks
can be attributed to partially cured networks, whereas a single peak indicates fully cured network [11].   In
composites, this mechanical loss parameter, or tan δ, is influenced by the incorporation, type and distribution
of the fibers, as well as the interaction fiber/matrix and void content. Below Tg, the conversion of energy is
low, because, in this region, the segments of the chain are frozen, the deformations are primarily elastic and
sliding of the molecules resulting in viscous flow is low [11]

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

Figure 8: Tan δ curves of the C4 (a) and post-cured C4 (b) composites for different frequencies.

Figure 9: Tan δ curves of the C6 (a) and post-cured C6 (b) composites for different frequencies.

4. CONCLUSIONS

This paper focused on the thermal-mechanical characteristics of a vinyl ester resin and composites reinforced
with glass fiber using mainly DSC and DMA analyses, which were used to verify the effect of the postcuring on composite characteristics. The need for post-curing was justified, for instance, by the purge of residual enthalpy of the curing reaction and a significant increase in storage modulus (around 39%). Postcuring increased crosslinking degree, yielding a more rigid material less susceptible to premature failure.

The gel time and gel temperature of the uncured resin were determined by the Society of the Plastics
Industry (SPI) method, which is a more readily available technique than DMA, even though usually regarded
as non-reliable. Nevertheless, comparison between these two methods revealed very similar results, indicating suitability of the simpler and cheaper SPI method to evaluate gel time.

5. ACKNOWLEDGMENTS

The authors would like to thank CNPq, CAPES and FAPERGS for the financial support.

6. BIBLIOGRAPHY

[1] MAZALI, C.A.I., FELISBERTI, M.I., “Vinyl ester resin modified with silicone-based additives: III. Curing kinetics”, _European Polymer Journal_, v. 45, n. 8, pp. 2222-2233, Aug. 2009.

GARAY, A.C.; PAESE, L.T.; SOUZA, J.A; AMICO, S.C. revista Matéria, v.20, n.1, pp. 64 – 71, 2015.

[2] SULTANIA, M., RAI, J.S.P., SRIVASTAVA, D., “Studies on the synthesis and curing of epoxidized
novolac vinyl ester resin from renewable resource material”, _European Polymer Journal_, v. 46, n. 10, pp.
2019-2032, Oct. 2010.

[3] BOYARD, N., MILLISCHER, A., SOBOTKA, V., et al., “Behaviour of a moulded composite part: Modelling of dilatometric curve (constant pressure) or pressure (constant volume) with temperature and conversion degree gradients”, _Composites Science and Technology_, v. 67, n. 6, pp. 943-954, May 2007.

[4] VISCO, A.M., CAMPO, N., CIANCIAFARA, P., “Comparison of seawater absorption properties of
thermoset resins based composites”, _Composites Part A-Applied Science and Manufacturing_, v. 42, n. 2, pp.
123-130, Feb. 2011.

[5] SCOTT, T.F., COOK, W.D., FORSYTHE, J.S., “Kinetics and network structure of thermally cured vinyl
ester resins”, _European Polymer Journal_, v. 38, n. 4, pp. 705-716, Apr. 2002.

[6] CRAWFORD, S., LUNGU, C.T., “Influence of temperature on styrene emission from a vinyl ester resin
thermoset composite material”, _Science of the Total Environment_, v. 409, n. 18, pp. 3403-3408, Aug. 2011.

[7] GARAY, A.C., HECK, V., ZATTERA, A.J., SOUZA, J.A., AMICO, S.C., “Influence of calcium carbonate on RTM and RTM light processing and properties of molded composites”, _Journal of Reinforced_
_Plastics and Composites_, v. 30, n. 14, pp. 1213-1221, Jul. 2011.

[8] NAFFAKH, N., DUMON, M., GÉRARD J., “Study of a reactive epoxy-amine resin enabling in situ dissolution of thermoplastic films during resin transfer moulding for toughening composites”, _Composites Sci-_
_ence and Technology_, v. 66, n. 10, pp. 1376-1384, Aug. 2006.

[9] ORNAGHI, H.L., SILVA, H.S.P.da., ZATTERA, A.J., et al., “Dynamic mechanical properties of curaua
composites”, _Journal of Applied Polymer Science_, v. 125, n. 2, pp. E110-E116, Sep. 2012.

[10] COOK, W.D., SCOTT, T.F., QUAY-THEVENON, S., et al., “Dynamic mechanical thermal analysis of
thermally stable and thermally reactive network polymers”, _Journal of Applied Polymer Science_, v. 93, n. 3,
pp. 1348-1359, Aug. 2004.

[11] SCOTT, T.F., COOK, W.D., FORSYTHE J.S., “Effect of the degree of cure on the viscoelastic properties of vinyl ester resins”, _European Polymer Journal_, v. 44, n. 10, pp. 3200-3212, Oct. 2008.

[12] LAZA, J.M., JULIAN, C.A., LARRAURI, E., et al., “Thermal scanning rheometer analysis of curing
kinetic of an epoxy resin: 2. An amine as curing agent”, _Polymer_, v. 40, n. 1, pp. 35-45, Jan. 1999.

[13] GU, H., “Dynamic mechanical analysis of the seawater treated glass/polyester composites”, _Materials &_
_Design_, v. 30, n. 7, pp. 2774-2777, Aug. 2009.

[14] DA SILVA, A.L.N., TEIXEIRA, S.C.S., WIDAL, A.C.C., et al., “Mechanical properties of polymer
composites based on commercial epoxy vinyl ester resin and glass fiber”, _Polymer Testing_, v. 20, n. 8, pp.
895-899, Dec. 2001.

본문 출처 PDF: PDF 보기 · 다른 PDF는 위 [PDF 업로드]로 올릴 수 있습니다.

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.