Investigation on Nano‐Self‐Lubricant Coating Synthesized by Laser Cladding and Ion Sulfurization

W2047073586 · 수집 2026-10-04 18:12:19

T10377 Metal and Thin Film Mechanics

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

The composite processing between laser cladding and low temperature (300°C) ion sulfurization was applied to prepare wear resistant and self‐lubricating coating. The microstructure, morphology, phase composition, valence states, and wear resistance of the composite coating were investigated by scanning electron microscopy (SEM), atomic force microscope (AFM), X‐ray diffraction (XRD), X‐ray photoelectron spectroscope (XPS), and friction and wear apparatus. The results indicate that the laser cladding Ni‐based coatings and the maximum hardness of 46.5 HRC were obtained when the percent of pure W powder was 10%, composed of columnar dendrites crystals and ultrafine dendritic structure. After ion sulfurization at 300°C for 4 h, the loose and porous composite coating is formed with nanograins and the granularity of all grains is less than 100 nm, which consists of γ ‐(Fe, Ni), M 23 C 6 carbides, FeS, FeS 2 , and WS 2 . Furthermore, the wear resistance of the composite coating is better than the laser cladding Ni55 + 10%W coating, and the friction coefficient and mass losses under the conditions of dry and oil lubrication are lower than those of laser cladding Ni55 + 10%W coating.

본문

PDF 본문 자동 추출 실패: [download] HTTP 403 Forbidden (2026-10-04 21:40:24)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.