MAGNETIC AND ELECTRICAL PROPERTIES OF ELECTRON BEAM GUN DEPOSITED [Mn/Al] MULTILAYERED FILMS

W1516673838 · 수집 2026-10-04 18:12:13

T13104 Chemical and Physical Properties of Materials

CoT 라벨링

라벨링 전

PDF 파일

저장된 PDF 없음

기본 정보

DOI 제목 발행년도 저널 URL 페이지 열기 PDF URL PDF 열기 발행기관 피인용수 라이선스

추가 정보 초록

By following electron beam gun evaporation technique, the magnetic multilayers in the configuration, [Mn(60nm)/Al(20nm)]n; n =1, 2 and 9 were deposited at 473K,Â under high vacuum conditions. From grazing incidence X- ray diffraction (GIXRD) studies, the grain sizes were determined and they were in the order of few nanometers. Atomic force microscope (AFM) were employed to study surface structure and grain sizes. The magnetization as a function of field at 150K and 200K have been measured using the MPMS SQUID - vibrating sample magnetometer (VSM). From the hysteresis loops, coercive field, saturation magnetization, remanent magnetization and antiferromagnetic coupling were determined. All the three films hinted at the existence of at antiferromagnetic interaction between Mn layers through Al layer. Electrical resistivity in the temperature range from 5K to 300K has been measured. Films exhibited semiconducting to metallic transition. The power law variation of resistivity with temperature was established for the metallic region. Conductivity data for semiconducting region of a film has been analysed using polaran hopping models, activation energy and density of states at Fermi level were established. This is for the first time that antiferromagnetic coupling between Mn layers through interfacer layer and semiconducting to metallic transition have been noticed in the present configuration of [Mn/Al] multilayers.

본문

PDF 본문 자동 추출 실패: [download] connection error: HTTPConnectionPool(host='japlive.com', port=80): Max retries exceeded with url: /index.php/jap/article/download/1487/pdf_166 (Caused by NameResolutionError("HTTPConnection(host='japlive.com', port=80): Failed to resolve 'japlive.com' ([Errno -2] Name or service not known)")) (2026-10-04 19:58:37)

활용가능성

이력 0건

아직 편집 이력이 없습니다. 저장할 때마다 이전 내용이 여기에 백업됩니다.